PETG 韓國SK JN200擠出級 物性認證數據表
| 性能項目 | 測試條件 | 測試方法 | 數值/描述 | 單位 | |
| 機械性能 | 拉伸強度(引張強度) | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | ||
| 斷裂伸長率 | ASTM D412/ISO 527 | 340 | % | ||
| 拉伸模量 | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
| 拉伸屈服伸長率(延伸率) | ASTM D412/ISO 527 | % | |||
| 拉伸斷裂伸長率(延伸率) | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
| 彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 18348 | kg/cm2(MPa)[Lb/in2] | ||
| 彎曲強度 | ASTM D790/ISO 178 | 683 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | 105 | kg·cm/cm(J/M)ft·lb/in | ||
| IZOD 缺口沖擊強度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/4" -30℃ | ASTM D256/ISO 179 | kg/cm2(MPa)[Lb/in2] | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| Charpy沖擊強度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 23℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.23 | ||
| 成型收縮率 | ASTM D955 | 0.002-0.005 | % | ||
| 光學性能 | 折射率 | ASTM D542/ISO 489 | |||
| 透光率 | ASTM D1003/ISO 13468 | % | |||
| 模糊系數（Haze） | ISO 14782 | % | |||
| 其他 | 備注 | ||||
| 顏色 | |||||
| 特性 | 光澤高，搞撞擊性強。 | ||||
| 用途 | |||||
SK PETG作為板材原料的介紹：PETG的另一個非常廣的用途就是板材。用PETG制成的板材，抗沖擊性能和韌性都非常突出，其抗沖擊性能是改性聚丙烯酸酯類的3到10陪。這種板材易于印刷和再加工，且具有同類塑料板中較好的環保性能。PETG板材與PC板和抗沖改性的壓克力不同，這種板材無須在熱成型加工前進行預干燥處理。與PC板或壓克力相比，其成型周期短，溫度低，成品率更高 ，PETG 作為異型材應用：可成型管材或各種型材，其制品堅硬、透明、光澤好，受壓不泛白，易于成型及后加工處理，符合環保要求，同時符合美國FDA關于食品接觸標準，廣泛應用于建筑裝飾及材料。
SK PETG用于吹瓶領域：
PETG材料的晶瑩剔透性決定了其必然會成為各類追求美觀的商品盛裝容器的受寵兒。PETG瓶有著傳統聚酯飲料瓶所不具備的韌性，再加上抗摔性好，可以任意作表面修飾，對人體無毒，可經常接觸，廣泛的應用于各類液態商品的包裝和盛裝，并在醫療領域也有應用。